Methods of making and using thermoplastic block copolymers

ABSTRACT

Methods of producing thermoplastic poly(amide-urethane) block copolymers having excellent flexibility at low temperatures are provided. The methods comprise reacting substantially linear polyamides, the polyamides being based on dimerized fatty acids and terminated by carboxyl and/or amino groups and aliphatic or cycloaliphatic polyethers and/or reaction products thereof with 2,3-epoxypropanol. The reaction products contain substantially no free isocyanate groups or epoxide groups. The invention also relates to the use of these products as adhesives and corrosion inhibitors for metallic and/or wooden materials.

This application is a division of Ser. No. 07/281,861, filed on Dec. 5, 1988, now U.S. Pat. No. 4,957,979; which is a continuation of Ser. No. 07/102,280, filed Sep. 28, 1987; which is a continuation of Ser. No. 06/829,377, filed on Feb. 13, 1986, both now abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to thermoplastic poly(amide-urethane) block copolymers which are characterized by excellent flexibility at low temperatures and by good adhesion to a wide variety of surfaces.

2. Description of Related Art

Thermoplastic polymers have been successfully used in the production of hotmelt adhesives and are widely used in industry for bonding a variety of materials and surfaces. Copolymers based on ethylene and vinyl acetate, copolyamides based on caprolactam, copolyesters based on terephthalic acid and other polybasic carboxylic acids and various glycols, polyurethanes and polyester urethanes, and polyamides based on dimer acids have all been successfully used in this field. However, the requirements which these materials must satisfy are becoming increasingly more stringent so that modifications are frequently necessary. For example, it is frequently necessary to improve the properties of the starting materials by the addition of other polymers to a thermoplast base or by the incorporation of resins, plasticizers or other auxiliaries. In these modifications, particularly the modification of polyamides based on dimerized fatty acids, and optionally with the addition of sebacic acid and various amines, the thermoplast bases become incompatible, at certain desired temperature ranges, with other starting materials used for producing hotmelts.

U.S. Pat. No. 4,018,733 discloses a typical prior art hot melt adhesive composition comprising an acidic ethylene polymer, a polyamide, and a tackifier.

In order to obtain optimal properties, especially at low temperatures, and more particularly optimal properties for use in the adhesive field, the present invention seeks to solve the problem of reproducibly providing, by chemical modification, polyamides based on dimer acids and amines which do not have any of the above-mentioned disadvantages. More particularly, the invention seeks to provide block copolymers which are characterized by excellent adhesion to a wide variety of surfaces and which, in addition, have excellent flexibility at low temperatures. Finally, the invention seeks to provide block copolymers having excellent adhesion and cohesion properties and which afford corrosion protection to metals and wood.

DESCRIPTION OF THE INVENTION

These and other objects of the present invention are met by a method of making thermoplastic poly(amide-urethane) block copolymers having excellent flexibility at low temperatures and improved adhesion properties, comprising reacting:

a) a substantially linear polyamide, having terminal groups selected from the group consisting of amino and carboxy groups, the polyamide being based on a dimerized fatty acid and an aliphatic or cycloaliphatic diamine; and

b) one or more agents selected from the group consisting of substantially linear, isocyanate-terminated aliphatic polyethers and reaction products of the aliphatic polyethers with 2,3-epoxy propanol (glycidol); to form a block copolymer product containing substantially no free isocyanate groups or epoxide groups.

The processes of the present invention may be carried out either in a melt or in the presence of an aprotic solvent. Suitable solvents include, for example, aromatic hydrocarbons, such as toluene, xylene, nitrobenzene or chlorobenzene and esters, such as ethyl acetate, methyl propionate and, chlorinated hydrocarbons, such as methylene chloride or tetrachloroethane.

The reaction is generally carried out at a temperature of from about 40° C. to 150° C. and preferably at a temperature of about 70° C. to 100° C. over a period of about 30 minutes to 3 hours. To isolate the reaction products, the solvent is distilled off, preferably under reduced pressure, except in special cases where the reaction solution can be further used.

The thermoplastic poly(amide-urethane) block copolymers are preferably produced from substantially linear polyamides which have been obtained by the condensation of from about 20 to 49.5 mole l% of a dimerized fatty acid, from about 0.5 to 15 mole % of a monomeric fatty acid having a chain length of from about 14 to 22 carbon atoms and from about 20 to 49.5 mole % of an aliphatic or cycloaliphatic diamine containing from 2 to 40 and preferably from 2 to 12 carbon atoms in the molecule. The acid and amine numbers of the starting polyamides should be between about 0.3 and 50 and preferably between about 1 and 15. The dimerized fatty acids are derived from fatty acids containing from 14 to 22 carbon atoms, and preferably, 16 to 18 carbon atoms.

In the context of the invention, the term "block copolymers" includes copolymers having a block-like structure and obtained by polycondensation or polyaddition reactions.

The polyamides based on dimerized fatty acids may be modified in a known manner with regard to their acid component. To this end, condensation of the polyamides may be carried out in the presence of other carboxylic acids, namely mono- and dicarboxylic acids containing from 4 to 36 carbon atoms, such as sebacic acid, adipic acid and/or montanic acids of various chain lengths. However, these other carboxylic acids should be used in limited quantities of no more than about 25 mole %, and preferably, no more than about 15 mole %, based on the total acid component.

As examples of diamines which may be used in the production of the starting polyamides, particular preference is given to low molecular weight diamines such as ethylene diamine, propylene diamine, hexamethylene diamine and piperazine. In addition, so-called dimer acid diamines which are produced by hydrogenating dimerized fatty acids via their nitriles to the corresponding amines may also be used. Fatty acid diamines such as these are generally used in only limited quantities, together with the short-chain C₂ -C₁₂ diamines.

Polyether glycols derived from OH-terminated aliphatic diols are preferably used for the production of the substantially linear isocyanate-terminated aliphatic polyethers. The aliphatic diols contain from 2 to 6 carbon atoms and preferably from 3 to 4 carbon atoms in the carbon chain. The polyether glycols also may be prepared in a known manner by the polymerization of corresponding epoxides using II-acid compounds, but especially of the aliphatic diols themselves as starter molecules. These substantially linear polyether glycols are sold commercially and are available in a variety of molecular weights. The polyether glycols generally used are those having molecular weights of from about 300 to 400 and preferably from 1000 to 3000. These commercial polyether glycols are produced, for example, by the polyaddition of propylene oxide or by ring-opening polymerization of tetrahydrofuran. Examples of suitable polyether glycols include polyoxypropylene glycol and polyoxytetramethylene glycol.

The OH-terminated polyethers are then reacted in a known manner under anhydrous conditions and in the presence of known catalysts, such as benzoyl chloride, with diisocyanates in molar ratios such that the starting ratio of OH groups to NCO groups is from 1:1 to 1:2 and preferably from 1:1.1 to 1:1.6. Isocyanate-terminated polyethers (i.e. (poly)urethanes) are thus obtained. Examples of suitable compounds for reaction with the OH-terminated polyethers include commercially available diisocyanates such as tolylene diisocyanate, methylene diphenyl diisocyanate (diphenylmethane diisocyanate) and isophorene diisocyanate (3-isocyanato-3,5,5-trimethyl cyclohexyl isocyanate).

The reaction of the starting polyamides with the linear isocyanate-terminated aliphatic polyethers is preferably carried out in the presence of an organic aprotic solvent of the kinds mentioned above.

In one preferred embodiment, the isocyanate-terminated aliphatic polyether is first reacted with 2,3-epoxy propanol (glycidol) before reaction with the polyamide. Epoxide-terminated prepolymers are obtained by this preliminary reaction.

The production of the poly(amide-urethane) block copolymers in accordance with the invention is then carried out as described above. The poly(amide-urethane) block copolymers have the following characteristic structures (including in particular those derived from the "glycidol reaction"): ##STR1## where PA represents the polyamide chain and PUR the isocyanate-terminated polyether chain. The free terminal groups of "PA" and "PUR" derive automatically from the equivalent ratios, i.e., the terminal groups of the components used in the molar excess are present. Terminal amino groups or terminal carboxyl groups are preferred. Both diblock systems (PA--PUR) and multiblock systems, in particular PA--PUR--PA, are possible.

The reactions of the present invention provide block copolymers containing both ether and ester bonds and also carbonamide and possibly even urea bonds. Accordingly, the invention provides a process for producing a variety of block copolymers. In addition to their outstanding flexibility at low temperatures, the block copolymers are distinguished by resistance to a broad range of chemicals and outstanding adhesion properties to a wide variety of materials and surfaces, including metals and high molecular weight materials. Similarly remarkable is the cohesion of shaped structures, especially adhesive and coating layers, produced with the new block polymers.

It is thus possible to produce firmly adhering coatings, on a variety of substrates, which may be converted back to an adhesive state simply by heating.

The block polymers produced by the described process generally have softening points of from about 70° C. to 180° C. and preferably from about 80° C. to 140° C. The viscosity of the block cocopolymers at 210° C. is in the range of from about 1000 to 50,000 mPa.s and preferably in the range of from about 3000 to 40,000 mPa.s.

In addition to good adhesion to metals which has already been mentioned, the poly(amide-urethane) block copolymers also provide excellent adhesion to a variety of high-melting thermoplasts and to duroplasts. Thus, bonds may be be established with high-melting polyamides and polyterephthalates, polyethylene, polypropylene, polystyrene, polyvinyl chloride and also with a variety of rubbers, particularly synthetic rubbers, such as for example styrene-butadiene rubber (SBR) or ethylene-propylene-diene terpolymers (EPDM).

The glycidol-modified block copolymers according to the invention are distinguished by particularly high flexibility. In addition, their adhesion to metals is remarkable. Accordingly, they be used as hotmelt adhesives or even as coating materials. The block copolymers according to the invention may be used either in the form of a melt (hotmelt) or even powder lacquers. They may of course also be used as adhesives in suitable solvents, optionally with the addition of the usual auxiliaries.

It is indeed surprising that, by this form of modification which may also be described as a chemical combination, incompatible components such as fatty acids polyamides and polyurethanes can be made compatible with one another so that it is now possible to produce thermoplastic block polymers which are superior in many respects to known polymers and polymer mixtures.

Although certain embodiments of the invention have been selected for description in the examples hereinafter, it will be appreciated by those skilled in the art that these examples are merely illustrative of, but do not in any way limit, the scope of the present invention which is defined in the appended claims.

EXAMPLES

Isocyanate- or epoxide-terminated polyalkylene-glycol-based prepolymers, known per se or produced in a known manner, were reacted with amino- or carboxyl-terminated polyamides based on dimerized fatty acids in order to produce the block copolymers according to the present invention. Their production and characteristic properties are described hereinbelow.

Prepolymer A

In a 2-liter flask, 581 g of polyoxypropylene glycol having an average molecular weight of 2000 (OH number 55), 0.3 g of benzoyl chloride and 92 g of diphenylmethane diisocyanate were stirred in 450 ml of anhydrous ethylacetate at 65° C. A solution of the NCO adduct in ethylacetate (isocyanate content 0.5% by weight) having a solids content of 60% by weight was obtained after 3 hours. Corresponding solutions of the NCO adduct in xylene and in toluene were also prepared.

Prepolymer B

37 g of 2,3-epoxy propanol were added to the solution of the NCO adduct in ethylacetate described as prepolymer A, followed by stirring for 2 hours at 70° C. in an inert gas atmosphere. After stirring, the NCO content had fallen to zero. The epoxide number was 2.0.

Prepolymer C

103 g of diphenylmethane diisocyanate in 480 ml of anhydrous xylene and 0.3 g of benzoyl chloride were added to 618 g of polyoxytetramethylene glycol having an average molecular weight of 2000 (OH number 56.1), followed by stirring for 3 hours at 70° C. in the absence of moisture. 35.9 g of 2,3-epoxypropanol were added to the resulting solution which had a solids content of 60% by weight (NCO content 0.5%). After 3 hours at 65° C., the NCO content had fallen to zero.

Polyamides D, E and F were produced in a known manner by condensation at temperatures ranging from 180° C. to 210° C. The quantities of reactants used and the properties of the polyamides are set forth hereinbelow. The following methods were used to measure the polyamide properties:

Softening point (SP): ring- and ball-method according to ASTM E 28

Viscosity: Brookfield RVT, spindle 27

Mandrell breaking point: ASTM D 3111

Tensile shear strength: DIN 53283 at RT

Crosshead speed: 50 mm/sec.

All percentages reported are percent by weight. The properties of the reaction products are listed to the right. The dimerized fatty acid (C₁₈) contained 1% by weight of monomeric and 4% of trimeric components.

Polyamide D

    ______________________________________                                         73.0% dimerized fatty acid                                                                     SP: 105° C.                                             19.0% dimer fatty amine                                                                        Viscosity: 4,250 mPa · s                                              at 210° C.                                               8.0% ethylene diamine                                                                         Amine number: 5.2                                                              Mandrell breaking point: -30° C.                        ______________________________________                                    

Polyamide E

    ______________________________________                                         85.0% dimerized fatty acid                                                                     SP: 130° C.                                             10.0% piperazine                                                                               Viscosity: 5,000 mPa · s                                              at 210° C.                                               5.0% azelaic acid                                                                             Acid number: 4.0                                                               Mandrell breaking point: -10° C.                        ______________________________________                                    

Polyamide F

    ______________________________________                                         71.0% dimerized fatty acid                                                                     SP: 101° C.                                             19.0% dimer fatty amine                                                                        Viscosity: 3,300 mPa · s                                              at 210° C.                                              10.0% ethylene diamine                                                                         Amine number: 10.4                                                             Mandrell breaking point: -15° C.                        ______________________________________                                    

EXAMPLES 1-6

The production of poly(amide-urethane) block copolymers in accordance with the invention was carried out with stirring over a period of 1 or 2 hours at a temperature of 70° C. to 100° C. in an approximately 35% by weight solution in ethylacetate, toluene or xylene. The solvent was then distilled at a reduced pressure of 1.3 KPa. The type and quantity of the polyamide and prepolymer reactants, and the measured softening point, viscosity at 210° C. and Mandrell breaking point temperatures for Example 1-6 are presented in Table 1 below. The type of reaction solvent medium (ethylacetate=E, toluene=T, xylene=X) is shown in the last column of Table 1.

                                      TABLE 1                                      __________________________________________________________________________                              Softening                                                                             Mandrell                                                          Viscosity                                                                            Range  Breaking                                       Example                                                                             Polyamide                                                                             Prepolymer                                                                            mPa · s at                                                                  ring and ball                                                                         Point Reaction                                 No.  amount/type                                                                           amount/type                                                                           210° C.                                                                       in °C.                                                                         Temp. °C.                                                                     Medium                                   __________________________________________________________________________     1    180 g/D                                                                                33.4 g/B                                                                             5,225 95-100-101                                                                            -50°                                                                          X                                        2    100 g/E                                                                                20.0 g/B                                                                             5,820 122-125-127                                                                           -55°                                                                          T                                        3    180 g/F                                                                                33.4 g/B                                                                             3,660 89.5-93-95.5                                                                          -35°                                                                          X                                        4    180 g/D                                                                                33.4 g/A                                                                             5,060 99-102-103                                                                            -40°                                                                          E                                        5    225 g/D                                                                               120.0 g/A                                                                             35,000                                                                               86.5-99-103                                                                           -60°                                                                          T                                        6    180 g/D                                                                                33.4 g/C                                                                             6,300 96-101-102.5                                                                          -40°                                                                          X                                        __________________________________________________________________________

EXAMPLE 7

The products produced in accordance with Example 1 were formed into sticks measuring 11.3×60 mm which were used to form bonds between various materials by means of a commercial hotmelt gun. The values determined for tensile shear strength are presented in Table 2 for comparison with the values (In parentheses) obtained with the unmodified polyamide D.

                  TABLE 2                                                          ______________________________________                                                        Tensile Shear                                                                             Comparison                                                          Strength   Tensile Shear                                        Material       (N/mm.sup.2)                                                                              Strength (N/mm.sup.2)                                ______________________________________                                         Aluminum       12.8       (6.0)                                                Steel          13.1       (6.0)                                                Copper         6.2        (1.1)                                                Nitrile rubber 10.2       (2.9)                                                Polyvinyl chloride                                                                            6.2        (1.9)                                                (rigid)                                                                        Polystyrene    6.4        (2.3)                                                ______________________________________                                    

EXAMPLE 8

The tensile shear strength values in N/mm² of bonds formed from the melt on various metals are shown in Table 3 below for the products of Examples 3 to 6:

                  TABLE 3                                                          ______________________________________                                         Product of:                                                                               Al            Cu    Fe                                              ______________________________________                                         Example 3  8.4           4.0   7.5                                             Example 4  10.1          6.9   11.3                                            Example 5  19.0          8.4   21.4                                            Example 6  15.8          9.8   18.9                                            ______________________________________                                    

Although the present invention has been described in terms of a number of specific examples and embodiments thereof, it will be appreciated by those skilled in the art that a wide variety of equivalents may be substituted for the specific parts and steps of operation described herein, all without departing form the spirit and scope of the present invention, as defined in the appended claims. 

We claim:
 1. A thermoplastic poly (amide-urethane) block copolymer comprising: a) the residue of at least one polyamide block comprising at least one substantially linear polyamide having terminal groups selected from the group consisting of carboxyl groups and amino groups wherein the substantially linear polyamide comprises the residues of at least one dimerized fatty acid and at least one aliphatic or cycloaliphatic diamine; and b) the residue of at least one block selected from the group consisting of substantially linear, isocyanate-terminated polyurethane block formed from reaction of a diisocyanate with an aliphatic polyether diol and reaction products of the isocyanate terminated polyurethane block with 2,3-epoxy propanol.
 2. The thermoplastic block copolymer of claim 1, wherein the block copolymer has a structure represented by: ##STR2## wherein PA represents a polyamide chain and PUR represents a polyurethane chain.
 3. The thermoplastic block copolymer of claim 1, wherein the block copolymer has a structure represented by: ##STR3## wherein PA represents a polyamide chain and PUR represents a polyurethane chain.
 4. The thermoplastic block copolymer of claim 2 in the form of a PA--PUR diblock system.
 5. The thermoplastic block copolymer of claim 3 in the form of a PA--PUR diblock system.
 6. The thermoplastic block copolymer of claim 2 in the form of a PA--PUR--PA multiblock system.
 7. The thermoplastic block copolymer of claim 3 in the form of a PA--PUR--PA multiblock system.
 8. A thermoplastic block copolymer of claim 1 wherein the polyamide block comprises the residues of a condensation reaction product of from about 20 to about 49.5 mol % of a dimerized fatty acid, from about 0.5 to about 15 mole % of a monomeric fatty acid having from about 14 to about 22 carbon atoms and from about 20 to about 49.5 mole % of at least one aliphatic or cycloaliphatic diamine containing from 2 to about 40 carbon atoms.
 9. A thermoplastic block a polymer of claim 8 wherein the aliphatic or cycloaliphatic diamine which form the condensation reaction product contains from 2 to about 12 carbon atoms.
 10. The block copolymer of claim 1 wherein the substantially linear polyamide comprises an acid number or an amine number of from about 0.3 to about
 50. 11. The block copolymer of claim 10 wherein the substantially linear polyamide comprises an acid number or an amine number in the range of from about 1 to about
 15. 12. A block copolymer of claim 1 wherein the isocyanate-terminated linear polyurethane block comprises the reaction product of an aliphatic polyether diol with from about 1 to about 1.6 equivalents of a diisocyanate.
 13. A block copolymer of claim 12 wherein the linear isocyanate-terminated polyurethane block comprises polyoxypropylene glycol or a polyoxytetramethylene glycol residue.
 14. A block copolymer of claim 1 wherein the isocyanate-terminated linear polyurethane block comprises glycol residues having an average molecular weight in the range of from about 300 to about
 4000. 15. A block copolymer of claim 14 wherein the glycol residue has an average molecular weight in the range of from about 1000 to about
 3000. 16. A thermoplastic block copolymer of claim 1 wherein the isocyanate-terminated polyurethane block comprises the reaction product of at least one polyether with at least one diisocyanate selected from the group consisting of toluene diisocyanate and diphenylmethane diisocyanate.
 17. A hot-melt adhesive comprising a composition of claim
 1. 18. A hot-melt adhesive comprising a composition of claim
 8. 19. A hot-melt adhesive comprising a composition of claim
 15. 20. A hot-melt adhesive comprising a composition of claim
 16. 